Waterborne Inorganic Zinc Rich Steel Spray Paint Primer Zinc Grey

Categories Steel Spray Paint
Brand Name: Huisins
Model Number: HWP-P110
Certification: ROHS/SGS/ISO
Place of Origin: China
MOQ: 500 L
Price: negotiation
Payment Terms: T/T or L/C or D/P
Supply Ability: 2,0000MT per month
Delivery Time: 15 working days after received your payment
Packaging Details: 24.7KG/18L in 20L container
Main Raw Material: Inorganic Zinc-Rich
Standard film thickness: 40 microns dry ( 70 microns wet)
Application Method: Spray
Color: Multicolor
Type: Topcoat
Luster: Half Glazed
Theoretical spreading rate: 200
Solids (vol %): ≤0g/L
  • Product Details
  • Company Profile

Waterborne Inorganic Zinc Rich Steel Spray Paint Primer Zinc Grey

Waterborne Inorganic Zinc-Rich Primer-Zinc Grey Steel Spray Paint

Product Description

  1. A two pack inorganic silicate zinc primer and it is characterized by good resistance to corrosion
  2. VOC is 0 g/L

Intended Uses

  1. For use in steel bridge of railway
  2. For use in steel frame of road and bridge

Product Information

  1. Volume Solids 58%±3%
  2. Finish/Sheen matt
  3. Typical Film Thickness 40 microns dry ( 70 microns wet)
  4. Theoretical Coverage : 13.7㎡/L at typical film thickness
  5. Mix Ratio: 2.8:1(mass)
  6. Method of Application

Brush/Roller Need to coat several times to get film thickness

  1. Thinner : Not recommended .Use water only in exceptional circumstances(max 5% by volume)

  1. Drying Information 5°C 15°C 25°C 35°C

Touch Dry 1H 40min 20min 15min

Hard Dry 8H 4H 2H 2H

Pot Life 8H 6H 4H 4H

Overcoatings Data : Substrate Temperature

Overcoated By 5°C 15°C 25°C 35°C

Min Max Min Max Min Max Min Max

48H no 36H no 24H no 24H no

  1. Storage :Store in cool and dry conditions, Well ventilate. Keep away from hot and fire.Store temperature should be higher than 0°C.

Shelf Life: 12Months minimum at 25°C.Subject to re-inspection thereafter.

  1. Pack Size : Part A 50kg in 20L container

Part B 17.8kg in 20L container

Surface Preparation : The surface should be cleaned oil or grease, dust, and other foreign matter to keep clean and dry.


  1. The coating is applied when the circumstance temperature is higher than 0°C and the humidity is lower than 80%
  2. It must be ventilate above 8H at poor ventilation area
  3. The dry time and over coating interval may change according to the environment factors.
  4. Forbid to trample or pullute the surface of AF3-1 and coat the next paint before the film is hard dry.

Cheap Waterborne Inorganic Zinc Rich Steel Spray Paint Primer Zinc Grey for sale
Send your message to this supplier
Enter your email please.
To: Huisins New Material Technology Co., Limited
Characters Remaining: (0/3000)
Inquiry Cart 0